Effect of abrasive water jet turning process parameters on surface roughness and material removal rate of AISI 1050 steel

dc.contributor.authorKartal F.
dc.contributor.authorGökkaya H.
dc.date.accessioned2023-04-12T02:51:56Z
dc.date.available2023-04-12T02:51:56Z
dc.date.issued2015-01-01
dc.description.abstractThe purpose of this study was to optimize and determine the most important abrasive water jet turning (AWJT) operational parameters, such as nozzle diameter (0.75 and 1.3 mm), nozzle feed rate (5, 25 and 45 min<sup>-1</sup>), stand-off distance (2, 10 and 18 mm), abrasive flow rate (50, 150 and 350 g × min<sup>-1</sup>), and spindle speed (500,1500 and 2500 min<sup>-1</sup>), regarding machining efficiency parameters, namely, average surface roughness R<inf>a</inf> (μm) and material removal rate (mm<sup>3</sup> × min<sup>-1</sup>), using AISI 1050 steel workpieces machined by abrasive water jet turning. Taguchi L<inf>18</inf>(2<sup>1</sup> × 3<sup>4</sup>) orthogonal experimental design was used for the experimental design. Adequacy of the predicted linear regression model equations was tested using the method of ANOVA. These model equations were used to optimize the operational parameters of the surface roughness and material removal rate. Machinability charts, indicating the optimum processes with respect to the surface roughness and material removal rate for AISI 1050 steel workpieces, were developed and presented in this study. As a result of experimental studies, it is seen that nozzle feed rate proved to have the most significant impact on surface roughness by 48.7 %. Abrasive flow rate proved to have the most significant impact on material removal rate by 84.6 %. Using a nozzle diameter of 0.75 mm, the average surface roughness was improved while material removal rate decreased.
dc.identifier.doi10.3139/120.110777
dc.identifier.issn00255300
dc.identifier.scopus2-s2.0-84941955300
dc.identifier.urihttps://hdl.handle.net/20.500.12597/5822
dc.relation.ispartofMaterialpruefung/Materials Testing
dc.rightsfalse
dc.subjectAbrasive water jet turning (AWJT) | AISI 1050 steel | Average surface roughness | Material removal rate | Taguchi method
dc.titleEffect of abrasive water jet turning process parameters on surface roughness and material removal rate of AISI 1050 steel
dc.typeArticle
dspace.entity.typeScopus
oaire.citation.issue9
oaire.citation.volume57
person.affiliation.nameKastamonu University
person.affiliation.nameKarabük Üniversitesi
person.identifier.scopus-author-id55567906300
person.identifier.scopus-author-id14832541900
relation.isPublicationOfScopus8cdacb4f-b0bd-4c91-96cd-58057a60685a
relation.isPublicationOfScopus.latestForDiscovery8cdacb4f-b0bd-4c91-96cd-58057a60685a

Files