BENDING CHARACTERISTICS OF LAMINATED WOOD COMPOSITES CONSTRUCTED WITH BLACK PINE WOOD AND ARAMID FIBER REINFORCED FABRIC

Basit Görünüm
dc.contributor.authorKaraman, Abdurrahman
dc.contributor.authorYildirim, Mehmet Nuri
dc.contributor.authorTor, Onder
dc.date.accessioned2026-01-04T15:19:18Z
dc.date.issued2021-04-30
dc.description.abstractThe aim of this study was to determine the 4-point bending strength and modulus of elasticity in bending of Black pine wood laminated materials reinforced with aramid fiber was bonded using epoxy or polyurethane glues separately. The samples were prepared in accordance with the TS 5497 EN 408 (2006). The results of the study determined that the highest value for static bending strength was found in the laminated wood samples (83.94 N.mm-2) that were prepared using inter-layer aramid fiber reinforced polymer (AFRP) and epoxy glue. The highest value of modulus of elasticity in bending was found in the samples prepared with inter-layer epoxy and AFRP (10311.62 N.mm-2). It was observed that the samples parallel to the glue line of the laminated material showed higher performance compared to those perpendicular to the glue line. The data obtained as a result of this study demonstrated that aramid fiber reinforced Black pine wood laminated materials can be used in the building industry as building materials.
dc.description.urihttps://doi.org/10.37763/wr.1336-4561/66.2.309320
dc.identifier.doi10.37763/wr.1336-4561/66.2.309320
dc.identifier.endpage320
dc.identifier.issn1336-4561
dc.identifier.openairedoi_________::b3bea801084516aabc3875fb7fa04f53
dc.identifier.orcid0000-0002-5925-7519
dc.identifier.orcid0000-0002-9405-1081
dc.identifier.scopus2-s2.0-85105970048
dc.identifier.startpage309
dc.identifier.urihttps://hdl.handle.net/20.500.12597/38744
dc.identifier.volume66
dc.identifier.wos000647314500014
dc.language.isoeng
dc.publisherPulp and Paper Research Institute
dc.relation.ispartofWood Research
dc.rightsOPEN
dc.titleBENDING CHARACTERISTICS OF LAMINATED WOOD COMPOSITES CONSTRUCTED WITH BLACK PINE WOOD AND ARAMID FIBER REINFORCED FABRIC
dc.typeArticle
dspace.entity.typePublication
local.api.response{"authors":[{"fullName":"Abdurrahman Karaman","name":"Abdurrahman","surname":"Karaman","rank":1,"pid":{"id":{"scheme":"orcid","value":"0000-0002-5925-7519"},"provenance":null}},{"fullName":"Mehmet Nuri Yildirim","name":"Mehmet Nuri","surname":"Yildirim","rank":2,"pid":null},{"fullName":"Onder Tor","name":"Onder","surname":"Tor","rank":3,"pid":{"id":{"scheme":"orcid","value":"0000-0002-9405-1081"},"provenance":null}}],"openAccessColor":"gold","publiclyFunded":false,"type":"publication","language":{"code":"eng","label":"English"},"countries":null,"subjects":[{"subject":{"scheme":"FOS","value":"0106 biological sciences"},"provenance":null},{"subject":{"scheme":"FOS","value":"0401 agriculture, forestry, and fisheries"},"provenance":null},{"subject":{"scheme":"FOS","value":"04 agricultural and veterinary sciences"},"provenance":null},{"subject":{"scheme":"FOS","value":"01 natural sciences"},"provenance":null}],"mainTitle":"BENDING CHARACTERISTICS OF LAMINATED WOOD COMPOSITES CONSTRUCTED WITH BLACK PINE WOOD AND ARAMID FIBER REINFORCED FABRIC","subTitle":null,"descriptions":["<jats:p>The aim of this study was to determine the 4-point bending strength and modulus of elasticity in bending of Black pine wood laminated materials reinforced with aramid fiber was bonded using epoxy or polyurethane glues separately. The samples were prepared in accordance with the TS 5497 EN 408 (2006). The results of the study determined that the highest value for static bending strength was found in the laminated wood samples (83.94 N.mm-2) that were prepared using inter-layer aramid fiber reinforced polymer (AFRP) and epoxy glue. The highest value of modulus of elasticity in bending was found in the samples prepared with inter-layer epoxy and AFRP (10311.62 N.mm-2). It was observed that the samples parallel to the glue line of the laminated material showed higher performance compared to those perpendicular to the glue line. The data obtained as a result of this study demonstrated that aramid fiber reinforced Black pine wood laminated materials can be used in the building industry as building materials.</jats:p>"],"publicationDate":"2021-04-30","publisher":"Pulp and Paper Research Institute","embargoEndDate":null,"sources":["Crossref"],"formats":null,"contributors":null,"coverages":null,"bestAccessRight":{"code":"c_abf2","label":"OPEN","scheme":"http://vocabularies.coar-repositories.org/documentation/access_rights/"},"container":{"name":"Wood Research","issnPrinted":"1336-4561","issnOnline":null,"issnLinking":null,"ep":"320","iss":null,"sp":"309","vol":"66","edition":null,"conferencePlace":null,"conferenceDate":null},"documentationUrls":null,"codeRepositoryUrl":null,"programmingLanguage":null,"contactPeople":null,"contactGroups":null,"tools":null,"size":null,"version":null,"geoLocations":null,"id":"doi_________::b3bea801084516aabc3875fb7fa04f53","originalIds":["10.37763/wr.1336-4561/66.2.309320","50|doiboost____|b3bea801084516aabc3875fb7fa04f53"],"pids":[{"scheme":"doi","value":"10.37763/wr.1336-4561/66.2.309320"}],"dateOfCollection":null,"lastUpdateTimeStamp":null,"indicators":{"citationImpact":{"citationCount":4,"influence":2.7879306e-9,"popularity":4.7367137e-9,"impulse":1,"citationClass":"C5","influenceClass":"C5","impulseClass":"C5","popularityClass":"C4"}},"instances":[{"pids":[{"scheme":"doi","value":"10.37763/wr.1336-4561/66.2.309320"}],"type":"Article","urls":["https://doi.org/10.37763/wr.1336-4561/66.2.309320"],"publicationDate":"2021-04-30","refereed":"peerReviewed"},{"pids":[{"scheme":"doi","value":"10.37763/wr.1336-4561/66.2.309320"}],"type":"Article","urls":["https://doi.org/10.37763/wr.1336-4561/66.2.309320"],"refereed":"nonPeerReviewed"}],"isGreen":false,"isInDiamondJournal":false}
local.import.sourceOpenAire
local.indexed.atWOS
local.indexed.atScopus

Dosyalar

Koleksiyonlar

Publications