Akkaş M., Al Sudani F.R.A.Akkas, M, Al Sudani, FRA2023-05-092023-05-092021-01-012021.01.010350-820Xhttps://hdl.handle.net/20.500.12597/14332In this study, a powder mixture consisting of TiC (titanium carbide) and WC (tungsten carbide) reinforced AlCuNiFeCr was produced using the hot pressing technique. The AlCuNiFeCr powder mixture, TiC and WC were added at a rate of 5%, 10% and 15%, respectively. In order to produce and control to produce parameters have been produced having automation systems type of laboratory a hot pressing machine. Graphite moulds were used in production and sintering processes were carried out in a protective argon gas atmosphere. Composites were produced at a sintering temperature of 900 oC and under a pressure 35 MPa and for 4 minutes. To understand the microstructure and mechanical properties of produced specimens, their SEM and EDS analysis, XRD analysis, fracture surface SEM images, SEM mapping of elemental distribution and EDX spectrums, hardness, three-point bending, and corrosion tests were investigated. As a result, the best sample has been identified that belong to AlCuNiFeCr- 15% WC with great features.trueHigh-entropy alloy (HEA) | Hot pressing | Mechanical properties | TiC reinforcement | WC reinforcementEffect of hot pressing and reinforcement of TiC and WC on the mechanical properties and microstructure of alcufecrni heas alloyEffect of Hot Pressing and Reinforcement of TiC and WC on the Mechanical Properties and Microstructure of AlCuFeCrNi HEAs AlloyArticle10.2298/SOS2101019A10.2298/SOS2101019A2-s2.0-85103571968WOS:000655069100003193553