Islak S.Kir D.Çelik H.Çelik E.2023-04-122023-04-122012-09-240350820Xhttps://hdl.handle.net/20.500.12597/6086The aim of this work was to investigate the effect of cBN content and sintering temperature on the transverse rupture strength (TRS) of cBN/diamond cutting tools produced by hot pressing. The segments containing different cBN content were manufactured under 35 MPa pressure at 600, 650 and 700 °C with a 3 minutes sintering time. The TRS of segments were determined using three-point bending test. Microstructure and phase composition of fracture surface of segments were determined by scanning electron microscopy (SEM), and X-ray diffraction (XRD) analysis. The obtained results show that the TRS of the segments with cBN were higher than that of the segments with diamond.falseCBN/diamond cutting tools | Hotpressing | TrsArticle10.2298/SOS 1202235K2-s2.0-84866363792