Cicek O.2023-04-122023-04-122020-01-011536125Xhttps://hdl.handle.net/20.500.12597/4916The letter reports the performance assessment of Au/n-Si type Schottky Junction Structure (SJS) with and without the graphene-PVP layer, classified as SJS1 and SJS2 devices. The electronic parameters by using the developed LabVIEW based program were calculated from raw data of I-V, C-V and G/ω-V measurements at room temperature. According to Thermionic Emission (TE) theory, the graphene-PVP layer significantly modified the barrier height than the other structure. Using the Ohm's Law, it is found that the $R_{sh}$ magnitude increases, while the $R_{s}$ magnitude decreases for SJS2, according to SJS1 type device. Alternatively, using Cheung's and the modified Norde functions for the accuracy and reliability of the results, the obtained n, $\phi _{Bo}$, $R_{s}$ values by both equations are in good agreement. Using the C-2-V and G/ω-V characteristics, the magnitudes of the electronic parameters, such as $\phi _{Bo}\,_{{\rm{(C-V)}}}$, $V_{bi}$, $V_{D}$, $N_{D}$, $E_{F}$, $R_{s}$, etc., for the devices were calculated to supply more information. Also, the $C_{i}$ and $C_{ox}$ magnitudes were calculated 1.299 × 10-10 F and 1.192 × 10-10 F at 3 V and then, the interface layer thicknesses were obtained as 2.08 nm and 68.8 nm for SJS1 and SJS2, respectively. It can be concluded that the graphene-PVP layer significantly affects the quality and performance of Au/n-Si type SJS devices.falseC-V and G/ω-V characteristics | electronic properties | graphene-PVP | I-V | Schottky Junction StructureArticle10.1109/TNANO.2020.29720362-s2.0-85080117134